TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 5 mm/min
|
1220
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
1220
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
2
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
2
|
%
|
ASTM D 638
|
|
Tensile Modulus, 5 mm/min
|
122300
|
kgf/cm2
|
ASTM D 638
|
|
Flexural Stress, brk, 1.3 mm/min, 50 mm span
|
1890
|
kgf/cm2
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
99900
|
kgf/cm2
|
ASTM D 790
|
|
Hardness, Rockwell R
|
119
|
-
|
ASTM D 785
|
|
Taber Abrasion, CS-17, 1 kg
|
22
|
mg/1000cy
|
SABIC Method
|
|
Tensile Stress, yield, 5 mm/min
|
120
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 5 mm/min
|
120
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 5 mm/min
|
1.9
|
%
|
ISO 527
|
|
Tensile Strain, break, 5 mm/min
|
1.9
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
10000
|
MPa
|
ISO 527
|
|
Flexural Stress
|
180
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
9500
|
MPa
|
ISO 178
|
|
Hardness, H358/30
|
118
|
MPa
|
ISO 2039-1
|
|
Hardness, Rockwell R
|
119
|
-
|
ISO 2039-2
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, unnotched, 23°C
|
63
|
cm-kgf/cm
|
ASTM D 4812
|
|
Izod Impact, notched, 23°C
|
6
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, -30°C
|
5
|
cm-kgf/cm
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 23°C
|
50
|
cm-kgf
|
ASTM D 3763
|
|
Izod Impact, unnotched 80*10*4 +23°C
|
45
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, unnotched 80*10*4 -30°C
|
45
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, notched 80*10*4 +23°C
|
7
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 -30°C
|
6
|
kJ/m2
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
7
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm
|
6
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm
|
50
|
kJ/m2
|
ISO 179/1eU
|
|
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm
|
50
|
kJ/m2
|
ISO 179/1eU
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
Vicat Softening Temp, Rate B/50
|
200
|
°C
|
ASTM D 1525
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
212
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
200
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow
|
2.5E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, xflow
|
8.9E-05
|
1/°C
|
ASTM E 831
|
|
Thermal Conductivity
|
0.25
|
W/m-°C
|
ISO 8302
|
|
CTE, -40°C to 40°C, flow
|
2.5E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, -40°C to 40°C, xflow
|
8.9E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, 23°C to 80°C, flow
|
2.5E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, 23°C to 80°C, xflow
|
1.2E-04
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate A/50
|
220
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/50
|
200
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
200
|
°C
|
ISO 306
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
220
|
°C
|
ISO 75/Be
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
195
|
°C
|
ISO 75/Ae
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
200
|
°C
|
ISO 75/Af
|
|
Relative Temp Index, Elec
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact
|
140
|
°C
|
UL 746B
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.63
|
-
|
ASTM D 792
|
|
Specific Volume
|
0.61
|
cm3/g
|
ASTM D 792
|
|
Mold Shrinkage on Tensile Bar, flow (2) (5)
|
0.1 - 0.5
|
%
|
SABIC Method
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
Mold Shrinkage on Tensile Bar, xflow (2) (5)
|
0.4 - 0.8
|
%
|
SABIC Method
|
|
Mold Shrinkage, xflow, 3.2 mm (5)
|
0.5 - 1
|
%
|
SABIC Method
|
|
Melt Flow Rate, 250°C/5.0 kgf
|
42
|
g/10 min
|
ASTM D 1238
|
|
Density
|
1.63
|
g/cm3
|
ISO 1183
|
|
Water Absorption, (23°C/sat)
|
0.09
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH)
|
0.07
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 250°C/5.0 kg
|
29
|
cm3/10 min
|
ISO 1133
|
|
ELECTRICAL
|
Value
|
Unit
|
Standard
|
|
Volume Resistivity
|
>1.E+15
|
Ohm-cm
|
ASTM D 257
|
|
Dielectric Strength, in air, 3.2 mm
|
19
|
kV/mm
|
ASTM D 149
|
|
Dielectric Strength, in oil, 1.6 mm
|
24
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity, 100 Hz
|
3.8
|
-
|
ASTM D 150
|
|
Relative Permittivity, 1 MHz
|
3.7
|
-
|
ASTM D 150
|
|
Dissipation Factor, 100 Hz
|
0.002
|
-
|
ASTM D 150
|
|
Dissipation Factor, 1 MHz
|
0.02
|
-
|
ASTM D 150
|
|
Arc Resistance, Tungsten {PLC}
|
6
|
PLC Code
|
ASTM D 495
|
|
Hot Wire Ignition {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate {PLC}
|
4
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index (UL) {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
Volume Resistivity
|
>1.E+15
|
Ohm-cm
|
IEC 60093
|
|
Surface Resistivity, ROA
|
>1.E+15
|
Ohm
|
IEC 60093
|
|
Dielectric Strength, in oil, 0.8 mm
|
23
|
kV/mm
|
IEC 60243-1
|
|
Dielectric Strength, in oil, 1.6 mm
|
22
|
kV/mm
|
IEC 60243-1
|
|
Dielectric Strength, in oil, 3.2 mm
|
16
|
kV/mm
|
IEC 60243-1
|
|
Relative Permittivity, 100 Hz
|
3.8
|
-
|
IEC 60250
|
|
Relative Permittivity, 1 MHz
|
3.3
|
-
|
IEC 60250
|
|
Dissipation Factor, 50/60 Hz
|
0.001
|
-
|
IEC 60250
|
|
Dissipation Factor, 100 Hz
|
0.002
|
-
|
IEC 60250
|
|
Dissipation Factor, 1 MHz
|
0.01
|
-
|
IEC 60250
|
|
Comparative Tracking Index
|
175
|
V
|
IEC 60112
|
|
Comparative Tracking Index, M
|
125
|
V
|
IEC 60112
|
|
Relative Permittivity, 50/60 Hz
|
3.3
|
-
|
IEC 60250
|
|
FLAME CHARACTERISTICS
|
Value
|
Unit
|
Standard
|
|
UL Recognized, 94V-2 Flame Class Rating (3)
|
0.4
|
mm
|
UL 94
|
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
0.71
|
mm
|
UL 94
|
|
UL Recognized, 94-5VA Rating (3)
|
2
|
mm
|
UL 94
|
|
Glow Wire Flammability Index 960°C, passes at
|
1
|
mm
|
IEC 60695-2-12
|
|
Oxygen Index (LOI)
|
32
|
%
|
ISO 4589
|
|
UV-light, water exposure/immersion
|
F2
|
-
|
UL 746C
|